Títulos: | Dependence of the microporosity of activated carbons on the lignocellulosic composition of the precursors |
Autores/as: | Román Suero, Silvia Ledesma Cano, Beatriz Álvarez Murillo, Andrés Al-Kassir Abdulla, Awf Yusaf, Talal |
Palabras clave: | Carbón activado;Biomasa;Composición lignocelulósica;Activated carbon;Biomass;Lignocellulosic composition |
Fecha de publicación: | 2017 |
Editor/a: | MDPI |
Resumen: | Se preparó una serie de carbones activados mediante gasificación física con vapor de vapor en condiciones experimentales idénticas para comparar el desarrollo de poros de los caracteres de poda de almendros y los carbonos activados de cáscara de nuez. Los resultados obtenidos mostraron que la gasificación por vapor produce carbones microporosos en ambos casos, y el aumento de la temperatura provoca un aumento de los volúmenes de poros de los carbones activados, hasta un cierto grado de combustión. Este efecto fue más marcado para la cáscara de nuez, que dio lugar a carbones activados con valores de superficie aparentes de hasta 1434 m2. g-1. Además, se encontró un ligero ensanchamiento de la porosidad en bajos grados de combustión. Esta ampliación de poros fue más marcada en el caso de los carbones activados de la poda de almendros, que también tienen un alto volumen de macroporos. Se encontró que las propiedades lignocelulósicas y de porosidad de las materias primas pueden causar este comportamiento diferente hacia los procesos de activación. A series of activated carbons were prepared by physical steam gasification under identical experimental conditions to compare the pore development from almond tree pruning chars and walnut shell activated carbons. The results obtained showed that steam gasification yields microporous carbons in both cases, and the rise in temperature causes an increase of the pore volumes of the activated carbons, up to a certain degree of burn-off. This effect was more marked for walnut shell, which gave rise to activated carbons with apparent surface values of up to 1434 m2.g-1. Also, a slight widening of porosity was found at low burn-off degrees. This pore widening was more marked in the case of activated carbons from almond tree pruning, which also have a high macropore volume. It was found that the lignocellulosic and porosity properties of the raw materials can cause this different behavior towards activation processes. |
URI: | http://hdl.handle.net/10662/8690 |
ISSN: | 1996-1073 |
DOI: | 10.3390/en10040542 |
Colección: | DFIAP - Artículos DIMEM - Artículos |
Archivos
Archivo | Descripción | Tamaño | Formato | |
---|---|---|---|---|
en10040542.pdf | 2,18 MB | Adobe PDF | Descargar |
Este elemento está sujeto a una licencia Licencia Creative Commons